500mm Graphite Electrodes yokhala ndi Nipples
Kukana kwa okosijeni ndikwabwino, ndipo kugwiritsa ntchito ma electrode kumachepetsedwa kwambiri.Anasankha mkulu khalidwe zopangira, graphitization pa kutentha, otsika zili zosafunika
The 500mmRP graphite elekitirodi opangidwa ndi China Hexi Carbon Co., Ltd. ali otsika resistivity, madutsidwe wabwino, mkulu matenthedwe kutembenuka mlingo, mkulu node mphamvu, kukana makutidwe ndi okosijeni ndi otsika ma elekitirodi kumwa.Amagwiritsa ntchito zida zapamwamba kwambiri, zokhala ndi zonyansa zochepa.Thermal shock resistance index index ndi yabwino kwambiri, yomwe imatha kutengera malo osiyanasiyana osungunula, ndipo ngozi ya fracture ndiyotsika.Amakonzedwa ndi chida chothamanga kwambiri, chokhala ndi makina okhazikika.Zida zonse zamakina zimathanso kumaliza kukonza ma elekitirodi, koma kukonza njira yodulira ndikosiyana ndi electrode yamkuwa.Iwo ndi mpweya maelekitirodi, chifukwa cha madutsidwe wabwino wa graphite, kotero mu kumaliseche processing angapulumutse nthawi yambiri, chomwe ndi chimodzi mwa zifukwa ntchito graphite monga elekitirodi.Atha kugwiritsidwa ntchito kwambiri popanga zitsulo zamagetsi zamagetsi, silicon yamafakitale, galasi la quartz, corundum ndi mafakitale ena.
Kuyerekeza kwaukadaulo kwa RP Graphite Electrode 20″ | ||
Electrode | ||
Kanthu | Chigawo | Supplier Spec |
Mawonekedwe Odziwika a Pole | ||
Nominal Diameter | mm | 500 |
Max Diameter | mm | 511 |
Min Diameter | mm | 505 |
Utali Wadzina | mm | 1800-2400 |
Kutalika Kwambiri | mm | 1900-2500 |
Min Length | mm | 1700-2300 |
Kuchulukana Kwambiri | g/cm3 | 1.55-1.63 |
mphamvu yodutsa | MPa | ≥8.5 |
Young' Modulus | GPA | ≤9.3 |
Kukaniza Kwachindunji | µΩm | 7.5-8.5 |
Kuchulukitsitsa kwakukulu kwapano | KA/cm2 | 13-16 |
Kuthekera Kwamakono | A | 25000-32000 |
(CTE) | 10-6 ℃ | ≤2.4 |
phulusa | % | ≤0.3 |
Mawonekedwe Odziwika a Nipple (4TPI/3TPI) | ||
Kuchulukana Kwambiri | g/cm3 | ≥1.74 |
mphamvu yodutsa | MPa | ≥16.0 |
Young' Modulus | GPA | ≤13.0 |
Kukaniza Kwachindunji | µΩm | 5.8-6.5 |
(CTE) | 10-6 ℃ | ≤2.0 |
phulusa | % | ≤0.3 |